Shinko-Lac® ABS 3001MF
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ooCPOE_Shinko-Lac-ABS-3001MF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS 3001MF is a plating grade of ABS that is especially designed for electro plating of injection molding combined with very good mechanical, etching and thermal cycle properties. Typical applications of 3001MF include microphone components, knobs, dials and electronic oven handles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2450 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 41.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 65.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 69 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 180 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 240 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 90.0 | °C | ASTM D648 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 200 - 250 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 200 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa | |
| Injection Rate | Slow |
| Injection instructions |
|---|
| Injection rate should be set as slow as possible. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MOSTEN MA 350 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Yuyao PA 011BG30 | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| Network Polymers PS HIPS 90 0304 | Network Polymers, Inc. | PS (HIPS) | Network Polymers PS |
| Addisil™ IND 1070 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| K-vinyl 80 Deg C Rating Insulation (85-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |