Daelim Po1y® LH-144
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gW4YA4_Daelim-Po1y-LH-144.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®LH-144 is a high density polyethylene product,. It can be processed by profile extrusion molding and is available in the Asia-Pacific region. Typical application areas are: water pipes/pipes/drinking water. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.12 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | > 1000 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 883 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 290 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
| Additional Information |
|---|
| Tensile Elongation @ Brk, ASTM D638: >600%Notched Izod Impact, ASTM D256: >30 kg.cm/cmOIT, ASTM D2951, 200°C, Aluminum Pan: >40 min |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WanBlend® WHT-1170M | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| CP PRYME® Polypropylene PPC100NB-20M NAT | Chase Plastics Services Inc. | PP Impact Copolymer | CP PRYME® Polypropylene |
| Latiohm 66-10 H2 CNT G/35 | LATI S.p.A. | Nylon 66 | Latiohm |
| Plaslube® PA6/6 TS20 FR BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| POCAN® S 1506 000000 | LANXESS GmbH | PBT | POCAN® |