Vyncolit® SI 9042
| Category: | Silicone , Silicone |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gVwO7q_Vyncolit-SI-9042.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SI 9042 is a long fiberglass reinforced silicone molding compound, which meets the requirements of ASTM D5948, Type MSI-30. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.0 - 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 28.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 13800 | MPa | ASTM D790 |
| Flexural Strength (Break) | 75.0 | MPa | ASTM D790 |
| Compressive Strength | 90.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 260 | °C | ASTM D648 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 7.9 | kV/mm | ASTM D149 |
| -- 2 | 5.9 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 6.0E-3 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Additional Information |
|---|
| All ASTM properties listed were tested in accordance with ASTM D5948.Water Absorption, ASTM D570, 48 hrs, 50°C: 0.3%DTUL @264psi - Unannealed, ASTM D648, Post Baked, Compression Molded: >260°CDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 5.9 kV/mmDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 7.9 kV/mmDielectric Constant, ASTM D150, 1000000 Hz, dry: 4.5Dissipation Factor, ASTM D150, 1000000 Hz, dry: 0.006 |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 18.F | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| TAISOX 3314 | Formosa Plastics Corporation | LLDPE | TAISOX |
| APEX® 4112 | Teknor Apex Company | PVC, Flexible | APEX® |
| LONGLITE® PBT 2100-202B | CCP Group | PBT | LONGLITE® PBT |
| Pearlthane® D91T86 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® |