Elastollan® 1185A10
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gUdS2H_Elastollan-1185A10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® 1185A is specifically formulated for extruded profile, sheet and film applications. It exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1185A10 is rated UL-94 HB in vertical flame test for wall thickness of 1.5 mm. Elastollan® 1185A also conforms to the FDA food contact section, book 21, section 177.2600. Elastollan® 1185A also has NSF Standard 61 "Water Contact Material" certification. Elastollan® 1185A is supplied uncolored in diced or pelletized form. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 1.0 to 20 | g/10 min | |
| 190°C/8.7 kg | 1.0 to 10 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 20.7 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 29.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 30.0 | mg | ASTM D1044 |
| Abrasion - DIN | 25 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 66 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 9.65 | MPa | |
| 300% Strain | 21.4 | MPa | |
| Tensile Strength | 35.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 530 | % | ASTM D412 |
| Tear Strength 1 | 110 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -38.0 | °C | Internal Method |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 190 to 220 | °C | |
| Nozzle Temperature | 210 to 225 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA ABS 4134 70/35 (China) | MBA Polymers | ABS | MBA ABS |
| VENELENE® FD-4048 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE+LLDPE | VENELENE® |
| Ablebond 967-3 | Henkel Ablestik | Epoxy | Ablebond |
| ADDINYL C2 M20 V10 | ADDIPLAST | Nylon 66/6 | ADDINYL |
| Lotader® 3210 | Arkema | EBA | Lotader® |