| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® Vestolen A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ev2aix_SABIC-Vestolen-A-6060R-65307.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® Vestolen A 6060R 65307 (blue) is a grade which has a high density and a bimodal distribution of the molecular mass. Due to its profile of properties this material is typically used for drinking water piping. This material meets (inter)national standards for use in drinking water piping. MRS class ISO 12162 MPa = 10.0 (PE 100). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | |
| 190°C/5.0 kg | 0.35 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1030 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress (Yield, 2.00 mm, Compression Molded) | 24.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Yield, 2.00 mm, Compression Molded) | 9.0 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Compression Molded | 9.2 | kJ/m² | |
| 23°C, Compression Molded | 23 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 72.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 43.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 71.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 124 to 128 | °C | DIN 53765 |
| Oxidation Induction Time - Compression Molded (210°C) | > 20 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO 12162 |
| RAL Number | 5005 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PC CT306 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC Alloy | Nanjing Hongrui PC |
| ACCUTECH™ POL050G20L | ACLO Compounders Inc. | PC | ACCUTECH™ |
| Bergamid™ B70 G30 RD163 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| APEX® 65005 | Teknor Apex Company | PVC, Flexible | APEX® |
| Luranyl® HT 200 G2 | ROMIRA GmbH | PPE+Nylon 66 | Luranyl® |