VALOX™ PDR7904 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gSGXk8_VALOXPDR7904resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GF filled PBT grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 36 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 141 | MPa | Internal method |
| Tensile Elongation 2(Break) | 9.7 | % | Internal method |
| Flexural Modulus (6.40 mm) | 11000 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 93 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 200 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.5 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 23 | % | ASTM D229 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 49 - 77 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 10mm/min |
| 2 . | Type 1, 10mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HT143E | LyondellBasell Industries | PP Copolymer | Supol |
| Mylar® J (265 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| ENFLEX VL-120-65A | Ravago Group | PP+EPDM | ENFLEX |
| Grilon® BS EC | EMS-GRIVORY | Nylon 6 | Grilon® |
| Karina CLEAR PVC COMPOUND 85/205-IS-K3 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |