Generic Nylon 66+Nylon 6I/X - Glass Fiber
| Category: | Nylon 66+Nylon 6I/X , Polyamide 66 + PA 6I/X |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gP7qmq_Generic-Nylon-66-Nylon-6I-X---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66+Nylon 6I/X - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.28 to 1.85 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.10 to 0.31 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 3.5 to 5.0 | % | |
| Equilibrium, 23°C, 50% RH | 1.2 to 1.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 223 to 370 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8200 to 28000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 145 to 292 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.9 to 3.1 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 to 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 to 91 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 230 to 250 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 65.0 to 220 | °C | ISO 75-2/C |
| Continuous Use Temperature | 110 to 220 | °C | ASTM D794 |
| Melting Temperature | 260 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.0E-5 to 1.5E-5 | cm/cm/°C | |
| Transverse | 4.9E-5 to 9.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+12 to 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (23°C) | 33 | kV/mm | IEC 60243-1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 151 | RTP Company | PP, Unspecified | RTP |
| Anjacom® R195-H/GF30 | Almaak International GmbH | Nylon 66/6 | Anjacom® |
| ESTAPROP K 1280 T8 | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| DURANEX® 3100H | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Luranyl® KR 2460/3 | ROMIRA GmbH | PPE+PS | Luranyl® |