LNP™ LUBRICOMP™ KZL16 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gIISeD_LNP-LUBRICOMP-KZL16-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber, Milled Glass and 5% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KFL-4016 M Product reorder name: KZL16 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.4 | % | ASTM D955 |
| Across Flow : 24 hr | 1.6 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 | % | ISO 294-4 |
| Flow : 24 hr | 1.5 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.29 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6140 | MPa | ASTM D638 |
| -- | 5800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 56.3 | MPa | ASTM D638 |
| Yield | 49.0 | MPa | ISO 527-2 |
| Break | 56.3 | MPa | ASTM D638 |
| Break | 46.8 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.6 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 |
| Break | 2.6 | % | ASTM D638 |
| Break | 4.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5310 | MPa | ASTM D790 |
| -- | 6300 | MPa | ISO 178 |
| Flexural Strength | 92.7 | MPa | ASTM D790, ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.50 | ||
| vs. Itself - Static | 0.43 | ||
| Wear Factor - Washer | 920 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| 23°C 2 | 3.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D4812 |
| 23°C 3 | 17 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.10 | J | ASTM D3763 |
| -- | 2.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 133 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 147 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOYOBO Urethane A2064D | TOYOBO America, Inc. | PUR-Capro | TOYOBO Urethane |
| AKROMID® C3 GF 30 5 XTC natural (4499) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| Hanwha Total PP BI530 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| KEBAFLEX® E 55.1 | BARLOG plastics GmbH | TPV | KEBAFLEX® |
| MAJ'ECO EG368LA | AD majoris | Biodeg Polymers | MAJ'ECO |