KOPLA PP KPG1020
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGQgCN_KOPLA-PP-KPG1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PP KPG1020 is a Polypropylene material filled with glass fiber. It is available in Asia Pacific. Primary attribute of KOPLA PP KPG1020: Flame Rated. Typical application of KOPLA PP KPG1020: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 3530 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Melting Temperature | 163 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HT125E | LyondellBasell Industries | PP Copolymer | Supol |
| Zhongfa PA6 BZR25 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 6 | Zhongfa |
| Laticonther 52/11 GR/70 | LATI S.p.A. | PP Homopolymer | Laticonther |
| Petro Rabigh PP AR764 | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |
| POLYLAC® PA-757GJ08 | CHI MEI CORPORATION | ABS | POLYLAC® |