Menzolit® SMC 1650
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gBQQHp_Menzolit-SMC-1650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 1650 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor any heavy metals. Menzolit® SMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer" . It has been tested and found to be compliant for resistance to fungal defacement in accordance with the Standard test method BS EN ISO 846:1997. "Plastics - Evaluation of the Action of Microorganisms", and for resistance to bacterial defacement in accordance with the Standard test method "JIS Z 2801:2000. "Antimicrobial products - Test for antimicrobial activity and efficacy". Specific applications are parts within health care or sanitary equipment or furnitures. The glass content is on a level that combines good mouldability with good strength and stiffness properties. The compound is available in a varity of sanitary colours, for availability please contact your local menzolit team. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.050 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-4 |
| Tensile Stress (Yield) | 56.0 | MPa | ISO 527-4 |
| Flexural Modulus | 8000 | MPa | ISO 14125 |
| Flexural Stress | 136 | MPa | ISO 14125 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 61 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | |
| Glass Transition Temperature | 170 | °C | ISO 11357-2 |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Fiber Content | 20.0 | ISO 1172 | |
| Glow Bar | BH 2 <= 10 | IEC 60707-3 | |
| Material Designation | >UP-(MD+GF)57< | EN 14598-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 542N | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| Moplen RP241R | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Moplen HP422H | LyondellBasell Industries | PP Homopolymer | Moplen |
| YUPLENE® BX38A | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| NEXUS PP CPP8/2 | Nexus Resin Group, LLC. | PP Impact Copolymer | NEXUS PP |