MAJORIS CG408X
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g7fKS9_MAJORIS-CG408X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS CG408X is a high performance reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. MAJORIS CG408X has been developed especially for demanding applications in various engineering sectors. MAJORIS CG408X has high rigidity and impact strength, good dimensional stability, very good stiffness and good creep resistancy also at high temperatures. APPLICATIONS Product requiring very high overall mechanical performance such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.50 to 0.80 | % | |
| Flow : 2.00 mm | 0.10 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 126 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 9230 | MPa | ISO 178 |
| Flexural Stress | 207 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 64 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 163 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Rate | Moderate | ||
| Holding Pressure | 30.0 to 60.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 3220 | Formosa Plastics Corporation | LLDPE | TAISOX |
| TAROBLEND 45 X0 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| Electrafil® PA6 CF30 | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| Karina STRAW PVC COMPOUND 800-38/39-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OTECH ALLOY NT1000-60 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |