ElectriPlast® EP-CF/66
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mbtWHL_ElectriPlast-EP-CF-66.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-CF/66 is a polyamide 66 (nylon 66) product containing nickel-plated carbon fiber. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11900 | MPa | ASTM D638 |
| Tensile Strength (Break) | 111 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.4 | % | ASTM D638 |
| Flexural Modulus | 7830 | MPa | ASTM D790 |
| Flexural Strength | 199 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 290 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 250 | °C | ASTM D648 |
| CLTE - Flow | 1.9E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.37 | W/m/K | ASTM D5470 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.8E+2 | ohms | ESD STM11.11 |
| Volume Resistivity | 82 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 38 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (No Burn) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 282 | °C | |
| Middle Temperature | 288 | °C | |
| Front Temperature | 288 | °C | |
| Nozzle Temperature | 282 | °C | |
| Mold Temperature | 82.2 | °C | |
| Back Pressure | 3.03 | MPa | |
| Screw Speed | 170 | rpm |
| Injection instructions |
|---|
| Injection Speed: 2 in/sec1st Stage (injection): 2000 psi2nd Stage (molding): 450 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800EA (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Braskem PP RP 347 | Braskem | PP Random Copolymer | Braskem PP |
| Dugdale PVC Dynamic PVC Nitrile Flexible Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Geon™ Vinyl Rigid Extrusion 87554E | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Sylvin 8865-85FUV Orange 588 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |