TAFMER™ XM is a superior, low crystalline copolymer of propylene and alpha-olefin which is perfect for biaxially oriented polypropylene (PP) and cast film sealant as well as a resin modifier for polyolefins. TAFMER XM is developed with Metallocene catalyst. The material has excellent low temperature sealability, good sealing performance in a wide temperature range and good anti-blocking properties. As a heat seal layer for OPP film, TAFMER XM is an excellent package sealer for chocolates, cookies and crackers among other items. In addition, the low temperature shrink characteristics of PP can be improved with TAFMER XM.

Message

TAFMER™ XM is a superior, low crystalline copolymer of propylene and alpha-olefin which is perfect for biaxially oriented polypropylene (PP) and cast film sealant as well as a resin modifier for polyolefins. TAFMER XM is developed with Metallocene catalyst. The material has excellent low temperature sealability, good sealing performance in a wide temperature range and good anti-blocking properties. As a heat seal layer for OPP film, TAFMER XM is an excellent package sealer for chocolates, cookies and crackers among other items. In addition, the low temperature shrink characteristics of PP can be improved with TAFMER XM.

General Information
Features	High Clarity High Gloss High Hardness High Heat Resistance High Scratch Resistance Hot Tack Strength Low Temperature Heat Sealability Low to No Odor Low to No Taste
Uses	Film Packaging Sealants Shrink Wrap
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	7.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	55		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	390	MPa	ASTM D638
Tensile Strength			ASTM D638
Yield	13.0	MPa
Break	36.0	MPa
Tensile Elongation (Break)	> 600	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	74.0	°C	ASTM D1525
Melting Temperature	83.0	°C	ASTM D2117

Resin Grade	Manufacturer	Category	Trademark
POLYLAN T-19	POLYMA Kunststoff GmbH & Co. KG	ABS	POLYLAN
Relpet® QH5821	Reliance Industries Limited	PET	Relpet®
HiFill® PA6/12 CF30 BK	Techmer Engineered Solutions	Nylon 612	HiFill®
TECACOMP® PA66 TC black 4028	Ensinger GmbH	Nylon 66	TECACOMP®
ADENE® M15VQEGD00	A.D. Compound S.p.A.	PP Copolymer	ADENE®