Sumikon® PM-5900
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2TdzDL_SumikonPM5900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-5900 (Type JA Black) is Glass fiber and Inorganic filler filled resol resin (non-anmonia phenolic) molding compound. This grade is official registered UL with V-0 (t=3.0). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.47 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 57.0 | MPa | JIS K6911 |
| Flexural Modulus | 10000 | MPa | JIS K6911 |
| Flexural Strength | 102 | MPa | JIS K6911 |
| Compressive Strength | 185 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.2 | kJ/m² | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 9.0 | kV/mm | JIS K6911 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 6.0E+11 | ohms | JIS K6911 |
| -- 3 | 1.0E+11 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -G Melthene®-G | TOSOH Corporation | EVA | Melthene® -G |
| Duron PPE/PA 810 | ProPolymers Inc. | Nylon+PPE | Duron |
| Kingfa PBT G15 | Kingfa | PBT | Kingfa PBT |
| Laril 13 G/20-V1 | LATI S.p.A. | PPE+PS | Laril |
| WELLAMID Nylon 6600-PA66-GV 25 HWV0CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |