TITANCEED® mL3564
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Titan (M) Sdn. Bhd. |
| Trademark: | TITANCEED® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g2slBL_TITANCEED-mL3564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TITANCEED® mL3564 is a Linear Low Density Polyethylene material. It is available in Asia Pacific for cast film. Important attributes of TITANCEED® mL3564 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : Cast Film | 118 | MPa | |
| 1% Secant, TD : Cast Film | 137 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, Cast Film | 73.5 | MPa | |
| TD : Break, Cast Film | 46.1 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, Cast Film | 510 | % | |
| TD : Break, Cast Film | 680 | % | |
| Elmendorf Tear Strength - MD (Cast Film) | 0.0 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Cast Film) | 86 | ASTM D2457 | |
| Haze (Cast Film) | 2.4 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 to 310 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 102 CC | RTP Company | PP, Unspecified | RTP |
| Geon™ Vinyl Flexible A87F3 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| EPT X-3012P | Mitsui Chemicals, Inc. | EPDM | EPT |
| Mafill® CR XM 8144 | Ravago Group | PP, Unspecified | Mafill® |
| POLYblend PC/ABS 85FS GF10 | Polykemi AB | PC+ABS | POLYblend |