SCANAMID 66 A32^E Q30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polykemi AB |
| Trademark: | SCANAMID 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fzRYIF_SCANAMID-66-A32-E-Q30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 75 | -- | ASTM D2240 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | 80.0 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | 40 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4200 | 2000 | MPa | ISO 178 |
| Flexural Stress | 100 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -20°C | 9.0 | -- | kJ/m² | |
| 23°C | 11 | 16 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® C142-01N | Safripol (PTY) LTD | PP Impact Copolymer | Safron® |
| SHIN-A SE-70H | SHIN-A T&C | Epoxy | SHIN-A |
| Ultramid® 8234G HS | BASF Corporation | Nylon 6 | Ultramid® |
| Edgetek™ AS-000/000 AS BLACK | PolyOne Corporation | ABS | Edgetek™ |
| LubX® C extr. | Röchling Engineering Plastics SE & Co. KG | UHMWPE | LubX® |