TECHNYL® C 218 V30 BLACK 21N Datasheet,Nylon 6,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL® C 218 V30 Black 21N is a polyamide 6, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. The product offers an excellent combination between thermal and mechanical properties.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer
Features	Heat Stabilized - Inorganic Good dimensional stability Good liquidity Good demoulding performance
Uses	Electrical/Electronic Applications Connector Application in Automobile Field
Agency Ratings	EC 1907/2006 (REACH) UL QMFZ2
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
Resin ID (ISO 1043)	PA6-GF30

Physical	Dry	Conditioned	Unit	Test Method
Density	1.36	--	g/cm³	ISO 1183/A
Water Absorption				ISO 62
23°C, 24 hr	1.1	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.2	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	10000	6000	MPa	ISO 527-2/1A
Tensile Strength
Fracture, 23°C	170	--	MPa	ASTM D638
Fracture, 23°C	180	115	MPa	ISO 527-2/1A
Tensile Elongation
Fracture, 23°C	3.5	--	%	ASTM D638
Fracture, 23°C	3.2	6.5	%	ISO 527-2
Flexural Modulus
23°C	8900	--	MPa	ASTM D790
23°C	8500	4900	MPa	ISO 178
Flexural Strength
23°C	255	--	MPa	ASTM D790
23°C	250	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	10	18	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength
23°C	75	90	kJ/m²	ISO 179/1eU
23°C	70	--	kJ/m²	ISO 179/1fU
Notched Izod Impact
23°C	130	--	J/m	ASTM D256
23°C	9.0	19	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	218	--	°C	ISO 75-2/Bf
1.8 MPa, not annealed	205	--	°C	ASTM D648
1.8 MPa, not annealed	208	--	°C	ISO 75-2/Af
Melting Temperature	222	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+14	1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+13	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	--	22	kV/mm	IEC 60243-1
Relative Permittivity	3.80	4.50		IEC 60250
Dissipation Factor	0.020	0.090		IEC 60250
Comparative Tracking Index				IEC 60112
Solution a	600	600	V	IEC 60112
Solution B	475	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (0.40 mm)	HB	--		UL 94
Glow Wire Flammability Index (1.6 mm)	650	--	°C	IEC 60695-2-12
Oxygen Index	23	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	230 - 235	°C
Middle Temperature	235 - 240	°C
Front Temperature	240 - 250	°C
Mold Temperature	60 - 90	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	qxMH24_TECHNYLC218V30BLACK21N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TECHNO ABS 541	Techno Polymer Co, Ltd.	ABS	TECHNO ABS
TEREZ PA 6.6 7500 GF 35 HY	TER HELL PLASTIC GMBH	Nylon 66	TEREZ PA 6.6
Arlon® 1260	Greene, Tweed & Co.	PEEK	Arlon®
Flontech® FT-1-8	Guarniflon S.p.A. - Flontech Division	PTFE	Flontech®
Durethan® AKV 30 HR H2.0 900116	LANXESS GmbH	Nylon 66	Durethan®