TECACOMP® PEEK LDS black 3980
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fku69S_TECACOMPPEEKLDSblack3980.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | |
| Apparent Density | 0.90 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (380°C/10.0 kg) | 70 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (380°C/5.0 kg) | 34.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.48 | % | ISO 294-4 |
| Flow | 0.38 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/50 |
| Tensile Stress | 105 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 218 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | DIN 53765 |
| Melting Temperature | 343 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 100°C | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 200 to 260°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 260 to 300°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 100°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 200 to 260°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 260 to 300°C | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Service Temperature | |||
| long term | 260 | °C | |
| short term | 300 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Adhesion Strength - metal path | 19.4 | MPa | |
| Lazer Marking | |||
| Forward movement | 1.8 - 2.4 | m/sec | |
| Frequency | 120 - 180 | kHz | |
| Power | 2.00 - 8.00 | Watts |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.8E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 5.8E+13 | ohms·cm | DIN EN 61340 |
| Dielectric Strength | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | < 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 160 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 360 - 400 | °C | |
| Mold Temperature | 160 - 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® FG151L NC010 | DuPont Performance Polymers | Nylon 612 | Zytel® |
| Diakon® MG102 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Elastollan® 670 AWHU | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Westlake LDPE EF 311 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Braskem PE PROXESS 2606 | Braskem | LLDPE | Braskem PE |