Polimid A 30 GF
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Poliblend S.p.a. |
| Trademark: | Polimid A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fkcAUI_Polimid-A-30-GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polimid A 30 GF is a Polyamide 66 (Nylon 66) material filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America. Primary attribute of Polimid A 30 GF: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.80 | % | |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 160 | MPa | |
| Break | 160 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 2.5 | % | |
| Break | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 70 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 110 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/A120 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 260 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Without Load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3690 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Naxel PC1210 | Custom Resins Group | PC | Naxel |
| ETILINAS LL0220SA | POLYETHYLENE MALAYSIA SDN BHD | LLDPE | ETILINAS |
| Genestar™ TA104 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| Karina IVORY PVC COMPOUND 751-35/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |