Maxxam™ PP FR 7380-8001-ISO
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fh9DMf_Maxxam-PP-FR-7380-8001-ISO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene, flame retardant and low blooming |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 48 hours, 3.00mm) | 1.4 - 1.9 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C, 4.00 mm, Injection Molded) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C, 4.00 mm, Injection Molded) | 220 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C, 4.00 mm, Injection Molded) | 1150 | MPa | ISO 178 |
| Flexural Stress 2(23°C, 4.00 mm, Injection Molded) | 28.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 13 | kJ/m² | ISO 179/eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed, 4.00 mm) | 95.0 | °C | ISO 75-2/Bf |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | Internal method | |
| Glow Wire Flammability Index | 875 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200 T-70A Z NATURAL | RTP Company | TPU-Polyether | RTP |
| Silplus® 60 HS | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| TPUCO® TPUI-L75 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| Nylene® 421 HS | Custom Resins Group | Nylon 6 | Nylene® |
| LNP™ THERMOCOMP™ DF004XXC compound | SABIC Innovative Plastics Europe | PC | LNP™ THERMOCOMP™ |