NORYL™ PX1543F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fceqpc_NORYL-PX1543F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL™ PX1543F resin is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.066 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 25 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2410 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 190 | J/m | |
| 23°C | 320 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 110 | °C | ASTM D648 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 5 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Nozzle Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers Polyester NPP 60-2008 PETG | Network Polymers, Inc. | PETG | Network Polymers Polyester |
| Nivionplast® A R306G NATURALE | SO.F.TER. SPA | Nylon 66 | Nivionplast® A |
| ALFATER XL® A60I 4FC0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| LNP™ STAT-KON™ EX12406C compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| Comco ABS | Comco Nylon GmbH | ABS | Comco |