Borealis PE FG5223
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xguhw0_Borealis-PE-FG5223.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FG5223 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes Antioxidant and Anti-block additives. This grade is developed for production of lamination film. FG5223 has good heat sealing properties and hot tack strength. By mixing with FG5224 any desired level of friction can be obtained. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Secant Modulus | ASTM D882A | ||
| MD : 70 µm | 145 | MPa | |
| TD : 70 µm | 165 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 70 µm | 29.0 | MPa | |
| TD : 70 µm | 28.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm | 800 | % | |
| TD : Break, 70 µm | 1000 | % | |
| Dart Drop Impact (70 µm) | 260 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 70 µm | 2.0 | N | |
| TD : 70 µm | 9.0 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 122 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 70.0 µm) | 100 | ASTM D2457 | |
| Haze (70.0 µm) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA6 B3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| FRblend® PA66-1301 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 66 | FRblend® |
| Hifax TRC 103P 11BK03 | LyondellBasell Industries | PP Copolymer | Hifax |
| LUVOCOM® 1/CF/20/TF/15 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Polene LDPE SU 1018 | TPI Polene Public Company Limited | LDPE | Polene LDPE |