Category: | PP Copolymer , Polypropylene Copolymer |
Manufacturer: | SO.F.TER. SPA |
Trademark: | Polifor® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | fXRKG7_Polifor-C-30-TR-20-H-GRIGIO-7306.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Heat stabilized polypropylene copolymer, 20% mineral filled |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
Agency Ratings |
|
Appearance |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 28 | g/10 min | ASTM D1238 |
Molding Shrinkage | 1.2 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield) | 25.0 | MPa | ASTM D638 |
Tensile Elongation (Break) | 25 | % | ASTM D638 |
Flexural Modulus | 2300 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 50 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Vicat Softening Temperature | 70.0 | °C | ASTM D1525 1 |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating | UL 94 | ||
1.60 mm | HB | ||
3.20 mm | HB |
Injection | Nominal Value | Unit | |
---|---|---|---|
Rear Temperature | 200 | °C | |
Middle Temperature | 230 | °C | |
Front Temperature | 240 | °C | |
Mold Temperature | 40.0 to 60.0 | °C |
Note Message | |
---|---|
1 . | Rate A (50°C/h), Loading 2 (50 N) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Sarlink® TPV 24825N-1 | Teknor Apex Company | TPV | Sarlink® TPV |
ELASTOSIL® LR 3065/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
Halene P B202S | Haldia Petrochemicals Ltd. | PP Random Copolymer | Halene P |
Karina PVC COMPOUND COLOR WHITE - E-818-10/23-CRM-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
POLYfill PPH MGF5040 | Polykemi AB | PP Homopolymer | POLYfill |