Monprene® OM-10265-01
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f5hiSG_Monprene-OM-10265-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®OM-10265-01 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Monprene®The main characteristics of the OM-10265-01 are: flame retardant/rated flame. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A 1 | 62 | ASTM D2240 | |
| Shaw A 2 | 68 | ASTM D2240 | |
| Shore A, 5 seconds, 22°C, injection molding 3 | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4 | ASTM D412 | ||
| Transverse flow : Fracture | 8.27 | MPa | ASTM D412 |
| Flow : Fracture | 4.96 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Flow : Fracture | 540 | % | ASTM D412 |
| Transverse flow : Fracture 5 | 780 | % | ASTM D412 |
| Tear Strength | 31.5 | kN/m | ASTM D624 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00mm, all colors | HB | UL 94 | |
| 6.00mm, all colors | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 138 - 188 | °C | |
| Middle Temperature | 154 - 199 | °C | |
| Front Temperature | 154 - 216 | °C | |
| Nozzle Temperature | 154 - 221 | °C | |
| Processing (Melt) Temp | 166 - 221 | °C | |
| Mold Temperature | 10.0 - 32.2 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Moisture can degrade the material. Drying is suggested. This can be accomplished by placing the material in a desiccant dryer for 1 to 2 hours at140°F. |
| Note Message | |
|---|---|
| 1 . | Aging 0 hr at 22°C |
| 2 . | Aging 24 hr at 22°C |
| 3 . | Aging 24 hr at 22°C |
| 4 . | 510 mm/min |
| 5 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 GA4S01 | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Trovidur® PN | Röchling Engineering Plastics SE & Co. KG | PVC, Rigid | Trovidur® |
| Geon™ Vinyl Rigid Extrusion 87549 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| ENGAGE™ 7270 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| ADENE® O07MJBGD00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |