Salflex 525T
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Salflex Polymers Ltd. |
| Trademark: | Salflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f22YAI_Salflex-525T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Salflex 525T is a high density polyethylene product, which contains 25% talc filler. It can be processed by blow molding or extrusion and is available in North America. Typical application areas are: automotive industry. The main characteristics are: impact resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/21.6 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.8 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 91.0 | °C | ISO 75-2/B |
| Additional Information |
|---|
| Ash Content, ISO 3451/1A: 25%Elongation at Break, ISO 527: No Break |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 190 - 225 | °C | |
| Cylinder Zone 2 Temp. | 190 - 230 | °C | |
| Cylinder Zone 3 Temp. | 190 - 235 | °C | |
| Cylinder Zone 4 Temp. | 190 - 235 | °C | |
| Melt Temperature | 200 - 235 | °C | |
| Die Temperature | 190 - 235 | °C |
| Extrusion instructions |
|---|
| Blow Molding Mold Temperature: 50 to 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ K115HF | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| CEPLA CT-454 | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| Epolene® E-14E | Westlake Chemical Corporation | LDPE | Epolene® |
| KOPA® KN333MS | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| PermaStat® 2700-50A | RTP Company | TES | PermaStat® |