Escor™ 5000

Category:	EAA , Ethylene Acrylic Acid Copolymer Resin
Manufacturer:	ExxonMobil Chemical
Trademark:	Escor™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	epr4Qc_Escor-5000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Escor 5000 is mainly used for extrusion coating, coextrusion coating and extrusion compounding. It can be well bonded to polar substrates, aluminum foils, metal films, paper, steel and glass surfaces. Provides an excellent balance of adhesion to the surface of the substrate and interlayer adhesion to coextruded low density polyethylene and ethylene vinyl acetate. Excellent adhesive polymer in film.

General Information

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	8.2	g/10 min	ASTM D1238
Acrylic Acid Content	6.0	wt%	ExxonMobil Method

Legal statement
有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用

Extrusion instructions
Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Extrusion instructions

Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Resin Grade	Manufacturer	Category	Trademark
VAMPLEN 2528 V0 CB	Vamp Tech	PP, Unspecified	VAMPLEN
Gallonprene® GP210-4004	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Galloo GP-PP-1065	Galloo Plastics	PP, Unspecified	Galloo
3M™ Dyneon™ PTFE Compound TFX R4262	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE Compound
Durethan® BKV 230 DUS008 000000	LANXESS GmbH	Nylon 6	Durethan®