OMIKRON BG 73 NAT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TECNOPOL |
| Trademark: | OMIKRON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ecDN1e_OMIKRON-BG-73-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OMIKRON BG 73 is an homopolymer polypropylene reinforced with 30% of glass fibre for injection moulding, high processability. It is available in natura. Coloured on demand. OMIKRON BG 73 is suitable for moulding of items requiring stiffness and dimensional stability well as good aesthetic. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 87.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 5800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 12 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | > 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 9.00 - 11.0 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.500 - 1.00 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 500 322 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Formolene® LH5204 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| OmniCarb™ PC10UV | OMNI Plastics, LLC | PC | OmniCarb™ |
| Kinta NB6630G | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 66 | Kinta |
| Sylvin 8200-90UV Red 6259 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |