SMOKEGUARD™ III 1042 NATURAL
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | SMOKEGUARD™ III |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v13Lbw_SMOKEGUARD-III-1042-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A LEAD FREE, 75°C RATED, FLAME RETARDED COMPOUND INTENDED FOR PLENUM CABLE CONSTRUCTIONS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 - 1.61 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 67 - 73 | ASTM D2240 | |
| Shaw D, 15 seconds | 54 - 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 0.381 mm | 17.9 | MPa | ASTM D412 |
| 1.91 mm | 15.9 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture, 1.91mm | 210 | % | ASTM D412 |
| Fracture, 0.381mm | 190 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1(100°C, 240 hr) | -1.0 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 2(100°C, 240 hr) | -7.0 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -5.00 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.35 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 51 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 154 | °C | |
| Cylinder Zone 2 Temp. | 166 | °C | |
| Cylinder Zone 3 Temp. | 171 | °C | |
| Cylinder Zone 4 Temp. | 177 | °C | |
| Cylinder Zone 5 Temp. | 177 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 182 - 188 | °C | |
| Die Temperature | 177 | °C | |
| Extruder Screw Compression Ratio | 3.0:1.0 |
| Extrusion instructions |
|---|
| Melt temperatures is critical, at excessive temperatures foaming may occur. It may be necessary to adjust barrel temp to attain the desired melt temperature. Material should be dried prior to use |
| Note Message | |
|---|---|
| 1 . | Thickness: 15 mil |
| 2 . | Thickness: 15 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KEG-2000-60A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Unichem 3478-NAT000 | Colorite Polymers | PVC, Rigid | Unichem |
| Hifax TSOP EM1 G63083 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Lucobit 1233 | Lucobit AG | PE Copolymer | Lucobit |
| MAJORIS CE141 - 8229 | AD majoris | Polyolefin, Unspecified | MAJORIS |