NORYL™ EN95 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eUxD1w_NORYL-EN95-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low heat, extrusion grade PPO/HIPS alloy. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 280 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 100 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 108 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 105 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Processing (Melt) Temp | 210 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 2110 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Visico™ LE4421/LE4460/ LE4437 | Borealis AG | PE, Unspecified | Visico™ |
| Comco PA 6 G high impact | Comco-Plastic GmbH | Nylon 6 | Comco |
| Duron PEI 1110-WHT | ProPolymers Inc. | PEI | Duron |
| MAJORIS G420 | AD majoris | PP, Unspecified | MAJORIS |