ProPolymers PPA TI-35G
| Category: | PPA , Polyphthalamide |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | ProPolymers |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eIb4Im_ProPolymersPPATI35G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPA TI-35G is a 35% glass fiber reinforced hest stabilized polyphthalamide (PPA) resin. It has very high stiffness, tensile strength, and heat deflections temperature combined with low water absorption and creep. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.47 | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.10 | 0.10 | % | ASTM D955 |
| Transverse flow | 0.65 | 0.65 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | 0.25 | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | 125 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 221 | 193 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | 2.0 | % | ASTM D638 |
| Flexural Modulus | 10300 | 10300 | MPa | ASTM D790 |
| Flexural Strength | 317 | 262 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 80 | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1000 | 1000 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 285 | 285 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 264 | 264 | °C | ASTM D648 |
| Continuous Use Temperature | 166 | 166 | °C | |
| Peak Melting Temperature | 302 | 302 | °C | ASTM D3418 |
| CLTE - Flow | 1.8E-5 | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 351 | Wacker Chemie AG | Silicone | POWERSIL® |
| Viprene™ P90A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Novodur® 250 | Styrolution | ABS | Novodur® |
| NORYL™ PPX630 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL™ |
| Wanthane® WHT-1180EC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |