RTP 199 X 108935
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eE76FM_RTP-199-X-108935.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Gravity Compound |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6550 | MPa | ASTM D638 |
| Tensile Strength | 21.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 to 1.0 | % | ASTM D638 |
| Flexural Modulus | 5650 | MPa | ASTM D790 |
| Flexural Strength | 35.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 96 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITIKA Nylon 6 EX-8406G30 | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| AVALON® 95 AEU | Huntsman Corporation | TPU-Polyester | AVALON® |
| FORMULA P COMP 3220 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Geon™ Advex™ L6105 natural | PolyOne Corporation | PVC, Rigid | Geon™ Advex™ |
| Polygen SC73C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |