LNP™ THERMOCOMP™ DC0041PQ compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e1lGZh_LNP-THERMOCOMP-DC0041PQ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DC0041PQ is a compound based on Polycarbonate resin containing Carbon Fiber. Added feature of this grade is: Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DC0041PQ Product reorder name: DC0041PQ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 | % | |
| Across Flow : 24 hr | 0.36 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 21000 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 185 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 18000 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 260 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 500 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 86.0 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 275 to 300 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 30 to 63 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec HP-007 | Genesis Polymers | PP, HMS | SureSpec |
| Delrin® 300TE BK602 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Fainplast PVC RK 912 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Karina IVORY PVC COMPOUND 105852-35/1-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ADENE® O07UFBG-00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |