Luranyl® KR 2403 G4 TW 26343
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Luranyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | n0sLhu_LuranylKR2403G4TW26343.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Luranyl®KR 2403 G4 TW 26343 is a polyphenylene ether + PS (PPE + PS) material, and its filler is 20% glass fiber reinforced material. This product is available in Europe, and the processing method is injection molding. Luranyl®The main features of KR 2403 G4 TW 26343 are:
Luranyl®Typical application areas of KR 2403 G4 TW 26343 are: water pipes/pipes/drinking water |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/21.6 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (23°C, 3.20 mm) | 0.30 - 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 128 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.5 | % | ISO 527-2/5 |
| Flexural Stress 1(23°C) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 80°C) | 4.0E-5 - 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.22 | W/m/K | DIN 52612 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tritan™ MP100 | Eastman Chemical Company | Copolyester | Tritan™ |
| Tufpet PBT S1040P | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| Arak HDPE BL2 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Aurora PVC AP2130 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Durolon® IR2200 | Unigel Plásticos | PC | Durolon® |