Pearlthane® D91T80
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dr2oGo_Pearlthane-D91T80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® D91T80 is an aliphatic TPU, supplied in colourless natural pellets. In addition to typical TPU properties like outstanding abrasion loss, our PEARLTHANE® D91T80 offers excellent colour stability upon UV exposure. PEARLTHANE® D91T80 features a low density, fast processing and excellent elasticity properties. It has been specially designed for injection moulding process. Pearlthane® D91T80 is especially recommended for injection moulding applications such as automotive parts and a variety of high performance technical parts where short cycle times and complete UV resistance are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| 20°C | 1.11 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 30.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 84 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 4.50 | MPa | ASTM D412, ISO 527 |
| 300% strain | 9.50 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 700 | % | ASTM D412, ISO 527 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 135 - 145 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 170 | °C | |
| Front Temperature | 175 | °C | |
| Nozzle Temperature | 175 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing force: 30 tonsScrew diameter: 30 mmMaximum hydraulic pressure: 210 barMould: Plaque 120x120x2 mm |
| Note Message | |
|---|---|
| 1 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9810 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Mylar® EL-21 (1400 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Bionate® 55D | DSM Biomedical Inc. | PC+TPU | Bionate® |
| Hifax CA244 | LyondellBasell Industries | TPO (POE) | Hifax |
| Kepamid® 2330GFS | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |