ENGAGE™ 8207
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YKt7VZ_ENGAGE-8207.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™8207 polyolefin elastomer is an ethylene-octene copolymer with excellent flow properties and has a wide range of applications in general-purpose thermoplastic elastomers. after blending with polypropylene (PP) and polyethylene (PE), ENGAGE 8207 has particularly excellent impact resistance and is especially suitable for processing and application fields requiring slightly higher melt flow rate. ENGAGE 8207 has high filler addition and excellent electrical properties (after crosslinking). The product has excellent thermal aging properties, compression deformation and weather resistance. Main features:
Application field:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.870 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 8 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 66 | ASTM D2240 | |
| Shore D, 1 second, molded | 17 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 2.30 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 5.70 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 1100 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : Molding | 10.9 | MPa | ASTM D790 |
| 2% secant : Molding | 10.8 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 37.1 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -53.0 | °C | Internal method |
| Vicat Softening Temperature | 37.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 59.0 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 44.0 | °C | Internal method |
| Additional Information |
|---|
| 对无滑石粉产品测量的属性。 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | C mould |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9966-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vital-Line SHM2800 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| TYMAX® GT4157 | Westlake Chemical Corporation | LLDPE | TYMAX® |
| Karina BLACK PVC COMPOUND -E 700-48/1-T-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9266-70 Blue 8417 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |