Edgetek™ ET5200-5014 NC FD
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | doCZta_Edgetek-ET5200-5014-NC-FD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and customer-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications, flame-retardant products as well as customer-specific compounds. These compounds are based on selected engineering thermoplastic resins containing reinforcing fillers and/or special additives. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 19 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 2(23°C, 4.00 mm) | 1.2 - 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 3(23°C, 4.00 mm) | 1900 | MPa | ISO 527 |
| Tensile Stress 4(Yield, 23°C, 4.00 mm) | 26.0 | MPa | ISO 527 |
| Tensile Strain 5(Break, 23°C, 4.00 mm) | > 50 | % | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | > 17 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179 |
| Additional Information |
|---|
| Determination of algae resistance: very good resistance against algae with growth rate 0Determination method: SAN BIO 33/99 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | ±0,03 |
| 2 . | Bergmann method |
| 3 . | 1 mm/min |
| 4 . | 5 mm/min |
| 5 . | 5 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NGM30-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Nypol® PA B3 G10 V20 PRTA011 NT354 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Catalyst F/AC | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| ELASTOSIL® R 420/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| PENTAMID A GK30 H natur | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |