Sarlink® TPE EE-2340DN XRD (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | do3Zbv_Sarlink-TPE-EE-2340DN-XRD-PRELIMINARY-DATA-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink EE-2340DN XRD is a general purpose thermoplastic elastomer used in automotive applications. Sarlink EE-2340DN XRD is a high hardness grade with good UV resistance. This grade can be processed by extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore D, 1 second, injection molding | 43 | ISO 868 | |
| Shore D, 5 seconds, injection molding | 40 | ISO 868 | |
| Shore D, 15 seconds, injection molding | 39 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 5.98 | MPa | ISO 37 |
| Flow : 100% strain | 8.73 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 15.1 | MPa | ISO 37 |
| Flow : Fracture | 11.8 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 700 | % | ISO 37 |
| Flow : Fracture | 460 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 69 | kN/m | ISO 34-1 |
| Flow | 55 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 23 | % | ISO 815 |
| 70°C, 22 hr | 65 | % | ISO 815 |
| 90°C, 70 hr | 59 | % | ISO 815 |
| 125°C, 70 hr | 79 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -2.0 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -2.6 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 14 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 17 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -13 | % | ISO 188 |
| Flow : 125°C, 168 hr | -0.80 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | 12 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | 20 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -8.4 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -28 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -8.7 | % | ISO 188 |
| Flow : 125°C, 168 hr | -29 | % | ISO 188 |
| Change in Shore Hardness in Air | |||
| Support d, 110°C, 1008 hr 8 | 2.7 | ISO 188 | |
| Support d, 110°C, 1008 hr 9 | 2.6 | ISO 188 | |
| Support d, 110°C, 1008 hr 10 | 2.0 | ISO 188 | |
| Support d, 125°C, 168 hr 11 | 1.2 | ISO 188 | |
| Support d, 125°C, 168 hr 12 | 1.0 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 423 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 5 sec |
| 9 . | 15 sec |
| 10 . | 1 sec |
| 11 . | 15 sec |
| 12 . | 5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHM1332B | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Vital-Line |
| KOPA® KN332G25V0BK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| I. Stern 3220NB | I. STERN & CO. INC. | PP Copolymer | I. Stern |
| OmniLon™ PA6/6 GR23 FR All Colors | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Honghai CPE 130A | Weifang Honghai Plastics Technology Co., Ltd. | CPE | Honghai |