Tufpet PBT S1030U
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dlsMpG_Tufpet-PBT-S1030U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT S1030U is a polybutene terephthalate (PBT) material, which contains 30% glass fiber reinforced materials and 10% mineral fillers. This product is available in North America and is processed by injection molding. The main features of Tufpet PBT S1030U are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.25 - 0.85 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 106 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 9410 | MPa | ASTM D790 |
| Flexural Strength | 177 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.10 | ASTM D1894 | |
| With self-dynamics | 0.21 | ASTM D1894 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 96.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 98 | J/m | ASTM D256 |
| Unnotched Izod Impact | 610 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 215 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 189 | °C | ASTM D648 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.026 | ASTM D150 | |
| Arc Resistance | 127 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.790 mm) | HB | UL 94 |
| Additional Information |
|---|
| Coefficient of Linear Thermal Expansion, ASTM D696: 3 to 6 E-5 cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 303 | °C | |
| Middle Temperature | 230 - 303 | °C | |
| Front Temperature | 230 - 303 | °C | |
| Mold Temperature | 40.0 - 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 26 JE 1 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| Novablend™ 6602 | PolyOne Corporation | PVC, Rigid | Novablend™ |
| Kingfa PBT RG30 | Kingfa | PBT | Kingfa PBT |
| LNP™ THERMOCOMP™ RF0069S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Polifor® E 12 SR/10 UV NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |