ARCEL® LD (1.25 pcf)
| Category: | PS+PE , Polystyrene + PE |
| Manufacturer: | NOVA Chemicals |
| Trademark: | ARCEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GgqIce_ARCEL-LD-1-25-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARCEL® LD (1.25 pcf) is a Polystyrene + PE (PS+PE) material. It is available in North America for foam processing. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.0200 | g/cm³ | ASTM D3575 |
| Particle Size - 98% | 0.900 to 2.00 | mm | |
| VOC Content | |||
| Pentane | 7.5 | % | |
| Plasticizer | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain | 11 | % | ASTM C203 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture | 168 | N | ASTM D3763 |
| Tear Strength - at Maximum Load | 1.5 | kN/m | ASTM D3575 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 0.288 | MPa | ASTM D3575 |
| Flexural Strength | ASTM C203 | ||
| -- | 0.273 | MPa | |
| 5.0% Strain | 0.241 | MPa | |
| Compressive Strength | ASTM D3575 | ||
| 10% Strain | 0.114 | MPa | |
| 25% Strain | 0.132 | MPa | |
| 50% Strain | 0.191 | MPa | |
| 75% Strain | 0.412 | MPa |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 130 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilex M5000 | API Polymers, Inc. | PC | Michilex |
| Sindustris PE XL8081UC | Sincerity Australia Pty Ltd. | PE, Unspecified | Sindustris PE |
| Chemical Resources PET07611 | Chemical Resources, Inc. | PET | Chemical Resources |
| ELASTOSIL® M 4630 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| Plasmer 1045BM/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |