DuPure® L 76 A
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | DuPure® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dO7GA9_DuPure-L-76-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description DuPure L 76 A is a polypropylene homopolymer for extrusion and thermoforming applications with nucleation and an anti-electrostatic agent. DuPure L 76 A offers good stiffness and transparency. The product exhibits an excellent processability and good wall thickness distribution of the thermoformed parts. Applications DuPure L 76 A is suitable for: thermoformed packaging for e.g. diary products, lids and trays. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 74.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 9.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.7 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 16 | kJ/m² | |
| 23°C | 140 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 1.5 | kJ/m² | |
| 23°C | 3.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A |
| -- | 94.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm) | 49 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-124-28 | Quantum Composites Inc. | TS, Unspecified | Quantum Composites |
| 3M™ Dyneon™ PTFE Compound TF 4105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Bolv LDPE 277-73 | Shandong Jining Bolv Chemicals Co.,Ltd | LDPE | Bolv |
| DJSilicone NE-5160 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Flontech® FT-GL25-8 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |