RTP 205.3 UV
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DZfln3_RTP-205-3-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm, Injection Molded) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 9990 | MPa | ASTM D638 |
| Tensile Strength | 172 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 3.0 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 9300 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 850 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, injection molded | 260 | °C | ASTM D648 |
| 1.8 MPa, unannealed, injection molded | 249 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 274 - 293 | °C | |
| Middle Temperature | 274 - 293 | °C | |
| Front Temperature | 274 - 293 | °C | |
| Mold Temperature | 66.0 - 107 | °C | |
| Injection Pressure | 83.0 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC LDPE BF315 | LG Chem Ltd. | LDPE | SEETEC LDPE |
| Sup-tech B103F | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| Durez® 33840 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| HiFill® PEEK CF15 A | Techmer Engineered Solutions | PEEK | HiFill® |
| LNP™ LUBRICOMP™ DL002ER compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |