SABIC® HDPE CC860V
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dGHf0y_SABIC-HDPE-CC860V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE CC860V is typically used for the injection moulding of high demanding applications, such as caps & closures for still water applications. The material offers a good combination of stiffness and impact resistance. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 7.6 | g/10 min | |
| 190°C/5.0 kg | 21 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 90.0 | hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1300 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 30.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 15.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1500 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 4.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature (DSC) | 133 | °C | ISO 11357-3 |
| Enthalpy Change | 219 | J/g | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Anjacom® R050/75K | Almaak International GmbH | PC+ABS | Anjacom® |
| Kumho PPG 3602 | Korea Kumho Petrochemical Co., Ltd. | POP | Kumho PPG |
| Sylvin 8999-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polystyrene Crystal 1050T | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Starex LX-0760 | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |