SABIC® PPcompound 3320EH
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dCVkPb_SABIC-PPcompound-3320EH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 3320EH is a high flow talcum filled Polypropylene. The stifness, low emission and heat aging performance make it suited for use in applications at elevated temperatures and emission requirements. SABIC® PPcompound 3320EH is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.1 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 30.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 25.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 15 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/4A | ||
| 0°C, Injection Molded | 2.2 | kJ/m² | |
| 23°C, Injection Molded | 2.7 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 120 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 150 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3811 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| NEFTEKHIM PP 7445L (EPC57MA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Devcon Underwater Repair Putty (UW) | Devcon | Epoxy | Devcon |
| PEXTIN™ PBTG15-BK10 | Pier One Polymers, Inc. | PBT | PEXTIN™ |
| Osterlene® LLH1018SA | Osterman & Company | LLDPE | Osterlene® |