Category: | EVA , Ethylene Vinyl Acetate Copolymer |
Manufacturer: | Hanwha Chemical |
Trademark: | HANWHA EVA |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | d0cfDZ_HANWHA-EVA-1315.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
HANWHA EVA 1315 is manufactured by Dow autoclave high pressure process and designed for variety of foam molding application such as shoes and sandals etc EVA 1315 is well known for its excellent processability and high quality assurance. |
General Information | |
---|---|
Features |
|
Uses |
|
Agency Ratings |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 0.938 | g/cm³ | ASTM D1505 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
Vinyl Acetate Content | 15.0 | wt% | Internal method |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Durometer Hardness | ASTM D2240 | ||
Shaw A | 93 | ASTM D2240 | |
Shaw D | 39 | ASTM D2240 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Break) | 14.3 | MPa | ASTM D638 |
Tensile Elongation (Break) | 840 | % | ASTM D638 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Brittleness Temperature | < -76.0 | °C | ASTM D746 |
Vicat Softening Temperature | 66.0 | °C | ASTM D1525 |
Peak Melting Temperature | 88.0 | °C | ASTM D3417 |
Additional Information |
---|
Kneader Temperature: 90 to 110°CRoll Mill Temperature: 100°C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Radilon® S RV350 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
NOVADURAN® 5010R5 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
Akulon® F127 | DSM Engineering Plastics | Nylon 6 | Akulon® |
Escorene™ Ultra UL 7765 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
Laprene® 830000540 | SO.F.TER. SPA | SEBS | Laprene® |