Ultradur B 4300 G2 is an easy flowing injection molding PBT with 10% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. Applications Typical applications include timer dials, toggles, knobs, parts for thermostats, oven-door handles, toaster housings and grills.

General Information
Filler / Reinforcement	Glass Fiber, 10% Filler by Weight
Features	Good Dimensional Stability Good Flow Good Toughness High Rigidity
Uses	Electrical/Electronic Applications Handles Housings Knobs
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS Compliant
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.37	g/cm³	ASTM D792, ISO 1183
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg)	16.0	cm³/10min	ISO 1133
Molding Shrinkage
Flow : 3.18 mm	0.80	%
Across Flow	1.4	%	ISO 294-4
Flow	1.2	%	ISO 294-4
Water Absorption
Saturation	0.40	%	ASTM D570
Saturation, 23°C	0.40	%	ISO 62
Equilibrium, 50% RH	0.20	%	ASTM D570
Equilibrium, 23°C, 50% RH	0.20	%	ISO 62
Viscosity Number (Reduced Viscosity)	115.0	ml/g	ISO 1628

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	4500	MPa	ISO 527-2
Tensile Strength
Break, 23°C	90.0	MPa	ASTM D638, ISO 527-2
Break, -40°C	111	MPa	ISO 527-2
Tensile Elongation (Break, 23°C)	3.5	%	ASTM D638, ISO 527-2
Flexural Modulus
23°C	3930	MPa	ASTM D790
23°C	3900	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.0	kJ/m²	ISO 179
Charpy Unnotched Impact Strength			ISO 179
-30°C	38	kJ/m²
23°C	40	kJ/m²
Notched Izod Impact
23°C	48	J/m	ASTM D256
23°C	5.0	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed	220	°C	ASTM D648, ISO 75-2/B
1.8 MPa, Unannealed	200	°C	ASTM D648, ISO 75-2/A
Peak Melting Temperature	223	°C	ASTM D3418, ISO 3146
CLTE - Flow	4.5E-5	cm/cm/°C
RTI Elec			UL 746
0.750 mm	130	°C
1.50 mm	130	°C
3.00 mm	130	°C
RTI Imp			UL 746
0.750 mm	125	°C
1.50 mm	125	°C
3.00 mm	125	°C
RTI Str			UL 746
0.750 mm	125	°C
1.50 mm	125	°C
3.00 mm	140	°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity ¹	1.0E+13	ohms	ASTM D257, IEC 60093
Volume Resistivity
1.50 mm	> 1.0E+13	ohms·cm	ASTM D257
--	> 1.0E+13	ohms·cm	IEC 60093
Dielectric Constant			IEC 60250
100 Hz	3.60
1 MHz	3.60
Dissipation Factor			IEC 60250
100 Hz	1.2E-3
1 MHz	0.015
Comparative Tracking Index	300	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.50 mm	HB
3.00 mm	HB

Injection	Nominal Value	Unit
Drying Temperature	100 to 120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.040	%
Processing (Melt) Temp	250 to 270	°C
Mold Temperature	60.0 to 100	°C
Injection Pressure	3.50 to 12.5	MPa
Injection Rate	Fast
Back Pressure	< 1.00	MPa

Note Message
1 .	1.5 mm

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3582C	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
NYCOA Polyamide 7555 Nat	Nycoa (Nylon Corporation of America)	Nylon 12	NYCOA Polyamide
Atlac 711-05AS	Reichhold Chemicals, Inc.	Polyester, TS	Atlac
Geon™ Vinyl Flexible Y126 White 317	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
LNP™ LUBRICOMP™ KAL22M compound	SABIC Innovative Plastics	Acetal (POM) Copolymer	LNP™ LUBRICOMP™