HiFill® XRD POM 0161 LE YL149
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cuFIgx_HiFill-XRD-POM-0161-LE-YL149.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Acetal Copolymer , Proprietary Filler for X-Ray Detection, Low Extractables for FDA Compliant Applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 2.1 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 42.7 | MPa | |
| Break | 40.0 | MPa | |
| Tensile Elongation (Yield) | 25 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 110 | °C | |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 177 to 193 | °C | |
| Middle Temperature | 188 to 210 | °C | |
| Front Temperature | 182 to 199 | °C | |
| Nozzle Temperature | 177 to 204 | °C | |
| Processing (Melt) Temp | 193 to 216 | °C | |
| Mold Temperature | 82.2 to 121 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A22140 HR | 4Plas | Nylon 66 | 4MID® |
| INEOS HDPE T50-1000-178 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Jamplast JPLGABS | Jamplast, Inc. | ABS | Jamplast |
| LONGLITE® PMC T355J | CCP Group | Phenolic | LONGLITE® PMC |
| Sylvin 9604-85 Clear 8159 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |