Lanufene HDF-5116
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Ras Lanuf Oil & Gas Processing Company (RASCO) |
| Trademark: | Lanufene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cgykLf_Lanufene-HDF-5116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LANUFENE HDF 5116 is a high density polyethylene copolymer designed primarily for conversion into tough thin gauged blown films exhibiting high stiffness with good process-ability. LANUFENE HDF 5116 is suitable for general purpose of medium strength HDPE film applications such as bags, liners, barrier film, agricultural mulching film, Co-extrusion film, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.15 | g/10 min | |
| 190°C/21.6 kg | 16 | g/10 min | |
| Environmental Stress-Cracking Resistance (F50) | > 500 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Flexural Modulus | 1130 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 15 µm | 1400 | MPa | |
| 1% Secant, TD : 15 µm | 1700 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 15 µm | 35.0 | MPa | |
| TD : Break, 15 µm | 32.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 350 | % | |
| TD : Break, 15 µm | 500 | % | |
| Dart Drop Impact (15 µm) | 25 | g | ASTM D1709A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 180 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Visico™ LE4421M / Visico™LE4431M | Borealis AG | PE, Unspecified | Visico™ |
| NORYL™ PVX0800 resin | SABIC Innovative Plastics | PPE | NORYL™ |
| NYCOA Polyamide 2063 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| Cellophane™ 345DMS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Kepital® GD-52 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |