Rilsan® BMNO MED
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dx7FSG_Rilsan-BMNO-MED.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan® BMNO MED is a polyamide produced from a renewable source. This grade dedicated to injection offers the highest quality and it is specifically designed to meet the stringent requirements of the medical applications such as minimally invasive devices. Upon request letters regarding USP Class VI compliance can be provided. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 30°C, 24 hr, 2.00 mm | 0.80 | % | |
| Flow : 30°C, 24 hr, 2.00 mm | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 75 | ||
| Shore D, 15 sec | 68 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1280 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 41.0 | MPa | |
| Break | 58.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 1140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 189 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11, M, 12-010 | ISO 1874 | |
| Renewable Carbon Conent | 100 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® TinCo 50 | A. Schulman Europe | Nylon 6 | SCHULATEC® |
| Nanjing Hongrui PA66 A305 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Boltaron 4325 FM4910 Clear CPVC | Boltaron Performance Products | CPVC | Boltaron |
| ASI POLYETHYLENE LP 552-01 | A. Schulman Inc. | HDPE Copolymer | ASI POLYETHYLENE |
| Genestar™ G1500A-M61 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |