Sunny® PBT EB230-034
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | caky0G_Sunny-PBT-EB230-034.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP flame retardant reinforced polybutylene terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.61 | g/cm³ | ASTM D792 |
| 23°C | 1.61 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 to 0.60 | % | ASTM D955 |
| 23°C | 0.30 to 0.60 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 120 | MPa | ASTM D638 |
| -- | 120 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.9 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 9500 | MPa | ASTM D790 |
| -- 4 | 9800 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 180 | MPa | ASTM D790 |
| -- 5 | 186 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 6 | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 200 | °C | ASTM D648, ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 115 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 235 | °C | |
| Front Temperature | 220 | °C | |
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 3.2mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3000 | RTP Company | PMP | RTP |
| Milastomer™ C700BM | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Clyrell RC124H | LyondellBasell Industries | PP Random Copolymer | Clyrell |
| Idemitsu PS SEHI-121 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| ICORENE® N4506 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | ICORENE® |