LNP™ LUBRICOMP™ RFN16SXZ compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | c3SI61_LNP-LUBRICOMP-RFN16SXZ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* RFN16SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Heat Stabilized, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4216 HS Product reorder name: RFN16SXZ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.28 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.65 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10700 | MPa | ASTM D638 |
| -- | 9900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 161 | MPa | ASTM D638 |
| Break | 163 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.8 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8410 | MPa | ASTM D790 |
| -- | 9800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 247 | MPa | ASTM D790 |
| -- | 255 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.43 | ||
| vs. Itself - Static | 0.49 | ||
| Wear Factor - Washer | 159 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 2 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 870 | J/m | ASTM D4812 |
| 23°C 3 | 58 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.20 | J | ASTM D3763 |
| -- | 2.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 261 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 249 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 220 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Favorite BI523 | Favorite Plastics | PE Alloy | Favorite |
| Gravi-Tech™ GRV-UR-110-W | PolyOne Corporation | PUR, Unspecified | Gravi-Tech™ |
| KRATON® D1184 K | Kraton Polymers LLC | SBS | KRATON® |
| Sylvin 8200-90 Clear 8395 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9077-75 Yellow 4109 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |